Viewpoint: Controlling the martensitic transition in Heusler shape-memory materials

  • Antoni Planes, Departament d'Estructura i Constituents de la Matèria, Facultat de Física, Universitat de Barcelona, Diagonal 647, Barcelona, E-08028 Catalonia, Spain
Physics 3, 36
Understanding the electronic structure of shape-memory alloys promises magnetic control over their crystal structures and hence mechanical properties.
Illustration: Alan Stonebraker
Figure 1: Crystal structures and phase diagram of Ni-Mn-Sn. The shadowed area in the phase diagram is the region where Ni-Mn-Sn, on cooling, first becomes ferromagnetic and later transforms martensitically. (A) The L21 structure showing also the relationship with the tetragonal unit cell. (B) Tetragonal (L10) unit cell. (C) The tetragonal unit cell viewed from top. (D) The martensitic structure constructed from nanotwinned variants of the L10 structure.Crystal structures and phase diagram of Ni-Mn-Sn. The shadowed area in the phase diagram is the region where Ni-Mn-Sn, on cooling, first becomes ferromagnetic and later transforms martensitically. (A) The L21 structure showing also the relationship w... Show more

Magnetic shape-memory properties occur in magnetic materials undergoing a martensitic transition, which is a transition from a cubic atomic structure to a layered structure that is dominated by strain. These materials show a strong change of shape in response to an applied magnetic field. The shape change is caused either by inducing a structural martensitic transition, or by rearranging twin related domains in the martensitic state. In 1996, O’Handley and collaborators at MIT first suggested the possibility of magnetic control over the shape-memory effect in a ferromagnetic Ni2MnGa “Heusler” alloy [1]. Heusler alloys are ferromagnetic alloys based on a Heusler phase, which is an intermetallic phase (a solid phase containing two or more metals) with face-centered-cubic structure. O’Handley et al. were able to induce reversible deformations of 0.2% by application of magnetic fields below 1T. Since then, the study of Heusler alloys with magnetic shape-memory properties has become an active field of research with great richness of basic physics, together with technologically interesting possibilities for applications, such as sensors and actuators.

Only a few years after the effect was proposed, giant deformations of about 10% were obtained in similar compounds of a slightly different, nonstoichiometric composition [2], and currently, much effort is expended in search of new Heusler materials with improved properties. At present, it is known that almost any Ni-Mn-based Heusler alloy will show a martensitic transition at an appropriate off-stoichiometric composition. In addition, these materials show other interesting functional properties such as magnetoresistance [3] or magnetocaloric effects [4]. The complex behavior displayed by these materials is, to a large extent, a consequence of the strong coupling between magnetism and structure that arises from the martensitic transition as the sample is cooled. Now, in a paper published in Physical Review Letters, Mao Ye and Akio Kimura at Hiroshima University, together with collaborators at Tohoku University, the National Institute for Materials Science, and Tohoku Gakuin University, all in Japan, study the case of Ni2Mn1+xSn1-x alloys to elucidate the role of excess Mn ions in driving the martensitic transition [5].

Stoichiometric Heusler alloys have a generic formula X2YZ and display an L21 structure at high temperature (see structure A, Fig. 1). The magnetism is due to 3d electrons from X and/or Y elements. The martensitic transition is a first-order, diffusionless transition that occurs via a dominant shear mechanism. The actual final martensitic structure depends on the alloy composition. The observed structures can be described as modulated phases that, to a good approximation, can be constructed from nanotwinned variants of a tetragonal L10 phase (resulting in crystal structure D in Fig. 1, after twinning) [6]. In Ni-Mn- Z (where Z=Ga, In, Sn, Sb, …), there is a composition range where, on cooling, the system first becomes ferromagnetic, and at a lower temperature undergoes the martensitic transition. Unless the Z chosen is Ga, this range is very narrow and is located in the Mn-rich region. For Ni-Mn-Ga, the range is very broad and extends from the Mn-poor to the Mn-rich regions (see, for instance, Ref. [7]). Ni2MnGa is so far the only known stoichiometric Heusler alloy that shows a martensitic transition in the ferromagnetic state.

In Ni-Mn-based alloys, it can be assumed that magnetic moments are localized at Mn atoms that are magnetically coupled through an oscillatory interaction via conduction electrons. Consequently, the magnetic behavior of these alloys is extremely sensitive to the distance between Mn atoms [8,9] and shows some dependence on the Z constituent. In general, however, for compositions with excess Mn, the magnetic moment decreases at the transition on cooling due to closer-neighbors Mn-Mn positions (Fig. 1), which become antiferromagnetically coupled [10]. Furthermore, for some compositions a re-entrance into a paramagnetic martensitic phase has been observed [11]. The significant decrease in magnetization at the transition favors the possibility of inducing the reverse transition magnetically, thus enabling the occurrence of magnetic superelasticity [12,13].

A good control of the parameters that govern phase stability is necessary to optimize materials design and to improve their functional properties. This requires an in-depth knowledge of the complex microscopic mechanism driving the martensitic transition in these ferromagnetic Heusler alloys, and thus a deep understanding of the behavior of the electronic structure in the vicinity of the transition. While several theoretical approaches have been reported, experimental work lags behind. Recently, uv-photoemission measurements in a nearly stoichiometric Ni2MnGa single crystal have been reported [14]. At the intermediate premartensitic transition, results confirm a depletion of electronic states (formation of a shallow pseudogap) located slightly below the Fermi energy ( 0.3eV) associated with the reconstruction of Ni3d minority spin-electron states, as predicted by theory [15]. On further cooling, at the martensitic transition, the peak associated with the Ni3d minority spin-electrons disappears and the spectral weight shifts to slightly higher energies ( 0.8eV). This shift reflects Ni3d and Mn3d electronic contributions to the spin-up density of states. This is usually understood as a band Jahn-Teller mechanism and suggests a charge-density wave mechanism from Fermi surface nesting [15].

The paper by Ye et al. has extended the study of the role of electronic structure in martensitic transition of ferromagnetic Heusler systems to the case of Ni2Mn1+xSn1-x alloys by combining hard x-ray photoelectron spectroscopy and first-principle calculations [5]. The interest in these new results arises from the fact that the authors have explicitly considered the relevance of the excess Mn in driving the martensitic instability by investigating systems of selected compositions. The obtained temperature-dependent photoemission spectra show an abrupt decrease of the peak associated with minority Ni3d states at the martensitic transition (which occurs for x0.36). This is associated with a band splitting that decreases the total energy, thus stabilizing the lattice distortion associated with the transition. This corroborates the expectation that the martensitic instability is related to a band Jahn-Teller mechanism.

Perhaps more interesting is the fact that the high-temperature peak associated with 3d minority spins shows a systematic shift towards the Fermi energy when the excess Mn concentration increases from x=0 to 0.42. This shift nicely correlates with a decrease of lattice parameter of about 2%. The first-principle calculations of Ye et al. attribute the shift of the peak to the hybridization of Ni3d and 3d states of antiferromagnetically coupled Mn atoms located at Sn sites. These results demonstrate that excess Mn enables hybridization of electronic states that strongly affect the stability of the martensitic phase in Ni-Mn-Sn Heusler alloys. In contrast, it is worth noticing that the excess Mn has very little effect on the temperature at which the L21 phase becomes ferromagnetic.

Comparison of the results obtained in Ni2MnGa and Ni-Mn-Sn clearly reveals the importance of the Z constituent on the behavior of these Heusler shape-memory alloys. The relevance of the Z element on the stability range of the martensitic phase in Ni-Mn-based Heusler alloys has also been pointed out in Ref. [16]. From present photoemission results, one can speculate that the extent of hybridization between Mn and Ni electronic states that establishes the range of stability of the martensitic phase depends crucially on the choice of Z element. It is only in the case of Z as Ga that off-stoichiometry composition is not needed for the transition to occur. For compositions close to the 2- 1- 1 stoichiometry, when hybridization does not play a role, the instability towards the martensitic phase occurs in a two-step process through an intermediate martensitic phase at which a pseudogap is formed in the density of states. This requires Fermi surface nesting effects that seem to be optimized for a given high enough value of the magnetization [17]. Indeed, recent finite temperature first-principle calculations suggest that this premartensitic instability is only possible thanks to a delicate interplay between magnetic excitations that overcompensate vibrational entropy [18].

The latest results from Ye et al. are likely to open new avenues of investigation of the basic physics underlying magnetic shape-memory phenomena as well as other complex functional materials where electronic instabilities are usually responsible for emergent functionalities. Moreover, these results are expected to provide insight into the more general phenomenon of magnetoelasticity.


  1. K. Ullakko, J. K. Huang, C. Kantner, R. C. O’Handley, and V. V. Kokorin, Appl. Phys . Lett. 69, 1966 (1996)
  2. A. Sozinov, A. A. Likhachev, N. Lanska, and K. Ullakko, Appl. Phys . Lett. 80, 1746 (2002)
  3. C. Biswas, R. Rawat, and S. R. Barman, Appl. Phys . Lett. 86, 202508 (2005)
  4. A. Planes, L. Mañosa, and M. Acet, J. Phys. Condens. Matter 21 233201 (2009)
  5. M. Ye, A. Kimura, Y. Miura, M. Shirai, Y. T. Cui, K. Shimada, H. Namatame, M. Taniguchi, S. Ueda, K. Kobayashi, R. Kainuma, T. Shishido, K. Fukushima, and T. Kanomata, Phys. Rev. Lett. 104, 176401 (2010)
  6. S. Kaufmann, U. K. Rößler, O. Heczko, M. Wuttig, J. Buschbeck, L. Schultz, and S. Fälher, Phys . Rev. Lett. 104, 145702 (2010)
  7. P. Entel, V. D. Buchelnikov, M. E. Gruner, A. Hucht, V. V. Khovailo, S. K. Nayak, and A. T. Zayak, Mater. Sci. Forum 583, 21 (2008)
  8. E. Sasioglu, L. M. Sandratskii, and P. Bruno, Phys . Rev. B 70, 024427 (2004)
  9. V. D. Buchelnikov, V. V. Sokolovskiy, H. C. Herper, H. Ebert, M. E. Gruner, S. V. Taskaev, V. V. Khovaylo, A. Hucht, A. Dannenberg, M. Ogura, H. Akai, M. Acet, and P. Entel, Phys. Rev. B 81, 094411 (2010)
  10. S. Aksoy, M. Acet, P. P. Deen, L. Mañosa, and A. Planes, Phys. Rev. B 79, 212401 (2009)
  11. R. Y. Umetsu, R. Kainuma, Y. Amako, Y. Taniguchi, T. Kanomata, K. Fukushima, A. Fujita, K. Oikawa, and K. Ishida, Appl. Phys. Lett. 93, 042509 (2008)
  12. R. Kainuma, Y. Imano, W. Ito, Y. Sutou, H. Morito, S. Okamoto, O. Kitakami, A. Fujita, T. Kanomata, and K. Ishida, Nature 439, 957 (2006)
  13. T. Krenke, E. Duman, M. Acet, E. F. Wassermann, X. Moya, L. Mañosa, A. Planes, E. Suard, and B. Ouladdiaf, Phys . Rev. B 75, 104414 (2007)
  14. C. P. Opeil, B. Mihaila, R. K. Schulze, L. Mañosa, A. Planes, W. L. Hults, R. A. Fisher, P. S. Riseborough, P. B. Littlewood, J. L. Smith, and J. C. Lashley, Phys . Rev. Lett. 100, 165703 (2008)
  15. A. Ayuela, J. Enkovaara, and R.M. Nieminen, J. Phys . Condens. Matter 14, 5325 (2002)
  16. T. Krenke, X. Moya, S. Aksoy, M. Acet, P. Entel, L. Mañosa, A. Planes, Y. Elerman, A. Yücel, and E. F. Wassermann, J. Magn. Magn. Mater. 310, 2788 (2007)
  17. Y. Lee, J. Y. Rhee, and B. N. Harmon, Phys . Rev. B 66, 054424 (2002)
  18. M. A. Uijttewaal, T. Hickel, J. Neugebauer, M. E. Gruner, and P. Entel, Phys. Rev. Lett. 102, 035702 (2009)

About the Author

Image of Antoni Planes

Dr. Antoni Planes is a Professor of Physics in the Department d’Estructura i Constituents de la Matèria at the Universitat de Barcelona, Catalonia, where he leads a group in phase transitions. His recent research has focused on the study of phase transitions in systems with interplay between structure and magnetism, such as magnetic shape-memory and magnetocaloric materials. He is also active in the study of the influence of disorder in phase transitions, with the aim of understanding precursor phenomena and avalanche criticality in externally driven systems.

Read PDF

Subject Areas


Related Articles

Synopsis: A New Quantum Spin Liquid Candidate

Synopsis: A New Quantum Spin Liquid Candidate

Neutron scattering experiments reveal signatures of an exotic phase of matter in the pyrochlore magnet Ce2Zr2O7. Read More »

Synopsis: An Airless Test for 2D Superconductors

Synopsis: An Airless Test for 2D Superconductors

Researchers repurpose a scanning tunneling microscope to measure the Meissner effect in 2D films kept under vacuum, allowing for confirmation of superconductivity. Read More »

Viewpoint: Phonons Hum a Magnetochiral Tune

Viewpoint: Phonons Hum a Magnetochiral Tune

A chiral material exposed to a magnetic field allows phonons to travel faster in one direction than another, an effect that might be used to create an acoustic diode. Read More »

More Articles